EPIKOTE MGSREPAIRSET633 /TD00 0,430KG cartridge repair set
MGS Repairset 633 is an epoxy-based laminating resin system with the constituents EPIKOTE Resin MGS LR635 and EPIKURE Curing Agent MGS LH633. It contains no solvents or fillers and intended main application is hand lamination process in repairs of composite structures. The pot life is approx. 15 min at room temperature. Different temperatures will have an influence on the
pot life. As a rule of thumb, the pot life will be doubled / reduced to half by a decrease / increase of 10°C. After initial curing at room temperature, the manufactured components are workable and demoldable. The final properties, however, will only be reached after a postcure at temperatures of more than 40°C.
The curing agent is strongly colored in order to make identification of homogenous mixing possible, especially at the very beginning of the application process. The color is only a visual aid and is therefore not exactly specified. Therefore, variations from batch to batch are possible. Furthermore, the color is not stable and can change over time. This can be especially observed for high reactive curing agents like LH633 as used in this repairset and in addition due to UV radiation (like exposure to direct sunlight).
Accordingly, the color can generally change during shelf life, but this has no known effect on the overall performance and does not constitute a quality complaint.
Repairset633 is only to be used with the supplied static mixers which provide good mixing and low loss of pressure. The tip of the mixing nozzle can be cut for an adaption of the flow rate.
We recommend processing as follows:
Only fully transparent products should be used. A milky / cloudy appearance of the mixed resin can be an indication for crystallization which is a physical phenomenon and immanently possible when product is stored at lower temperatures. Prior mixing, crystallization can be reversed by slow heating of the product to approx. 40°C and there is no restriction to quality after removal of crystallization. It needs to be noted that product should not be used immediately after heating because the reactivity will be significantly increased. Allow to cool down prior usage. No problems are expected concerning compatibility (e. g. blistering, tearing or changes in color) when
Repairset633 is processed with gelcoats. However, comprehensive tests are indispensable. The materials have a shelf life of minimum 4 years, when stored in their originally sealed kits. The relevant industrial safety regulations for the handling of epoxy resins and hardeners are to be observed.
pot life. As a rule of thumb, the pot life will be doubled / reduced to half by a decrease / increase of 10°C. After initial curing at room temperature, the manufactured components are workable and demoldable. The final properties, however, will only be reached after a postcure at temperatures of more than 40°C.
The curing agent is strongly colored in order to make identification of homogenous mixing possible, especially at the very beginning of the application process. The color is only a visual aid and is therefore not exactly specified. Therefore, variations from batch to batch are possible. Furthermore, the color is not stable and can change over time. This can be especially observed for high reactive curing agents like LH633 as used in this repairset and in addition due to UV radiation (like exposure to direct sunlight).
Accordingly, the color can generally change during shelf life, but this has no known effect on the overall performance and does not constitute a quality complaint.
Repairset633 is only to be used with the supplied static mixers which provide good mixing and low loss of pressure. The tip of the mixing nozzle can be cut for an adaption of the flow rate.
We recommend processing as follows:
- Remove cap nut and plug.
- Attach mixer and secure with cap nut.
- Reject the first 5-15 grams until color is homogenous.
Only fully transparent products should be used. A milky / cloudy appearance of the mixed resin can be an indication for crystallization which is a physical phenomenon and immanently possible when product is stored at lower temperatures. Prior mixing, crystallization can be reversed by slow heating of the product to approx. 40°C and there is no restriction to quality after removal of crystallization. It needs to be noted that product should not be used immediately after heating because the reactivity will be significantly increased. Allow to cool down prior usage. No problems are expected concerning compatibility (e. g. blistering, tearing or changes in color) when
Repairset633 is processed with gelcoats. However, comprehensive tests are indispensable. The materials have a shelf life of minimum 4 years, when stored in their originally sealed kits. The relevant industrial safety regulations for the handling of epoxy resins and hardeners are to be observed.